Highly corrosion-resistant, colored thin film-coated steel sheet having excellent press-processability and spot-weldability

ABSTRACT

This invention provides a highly corrosion-resistant, colored thin film-coated steel sheet having excellent press-processability and spot-weldability, which comprises a plated steel sheet, a first layer of a sparingly soluble chromate film formed on surface(s) of the plated steel sheet and having a water soluble content of 1 to 30%, a Cr 6+  /Cr 3+  ratio of 0.01 to 1.0 and a total chromium build-up of 10 to 150 mg/m 2  on one surface, and a second layer of a 0.3 to 5 μ thick solid coating film formed of an organic solvent-type coating composition, the solid coating film being comprised, based on the weight of the nonvolatile content, of 
     (a) a urethanated epoxy ester resin having a number average molecular weight of 300 to 100,000: 30 to 90%, 
     (b) a hydrophilic polyamide resin having a polymerization degree of 50 to 1,000: 5 to 40%, 
     (c) a silica powder having an average particle diameter of 1 to 100 μm: 5 to 40%, 
     (d) a lubricant: 1 to 20%, and 
     (e) at least one member selected from a group consisting of inorganic, and insoluble azo-type, azolake-type or phthalocyanine-type organic pigments having an average particle diameter of 0.05 to 5 μm: 0.1 to 20%.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a highly corrosion-resistant surface-treated steel sheet having an unconventional appearance design and excellent functions such as press-processability, electrodeposition coatability and weldability, which is manufactured by forming a thin, uniformly colored coating film on surface(s) of a steel sheet plated with Zn, a steel sheet plated with a zinc-based alloy such as Zn-Cr, Zn-Ni, Zn-Fe, Zn-Al, Zn-Mg or the like, a steel sheet plated with a zinc-based composite containing a metal oxide such as SiO₂, TiO₂, ZrO₂, or the like, a steel sheet plated with Al, a steel sheet plated with alloyed zinc, or a steel sheet having a multilayer of these platings. Such a surface-treated steel has great usefulness in fields requiring its low cost and multifunctions.

2. Description of Related Art

Colored steel sheets have been employed to comply with users' need for omission of coating and high resistance to corrosion. And, recently, there, has also been an increasing need for the coloring of plated steel sheets. However, it has not been possible to use any conventional colored steel sheet in a manner in which plated steel sheets are used, since they usually have a film thickness of 5 μm or more and therefore have insufficient weldability and press-processability.

That is, Japanese Patent KOKOKU (Post-Exam. Publns.) Nos. Sho 45-24230, 47-6882, etc., propose zinc-rich coating compositions, which permit electrodeposition coating. However, the press-processability of these coating compositions is poor and their corrosion resistance and weldability are also insufficient. Japanese Patent KOKOKU (Post-Exam. Publn.) No. Sho 52-44569, Japanese Patent KOKAI (Laid-Open) No. Sho 58-138758, Japanese Patent KOKOKU (Post-Exam. Publn.) Nos. Sho 54-9616 and 58-19706, etc., propose coating compositions incorporating an electrically conductive pigment, which remarkably improve the corrosion resistance of a zinc-plated steel sheet, etc., and also improve the weldability. Since, however, these coating compositions contain a comparatively large-sized pigment such as a zinc powder, metal powder, metal carbide, metal phosphide, or the like, films formed by electrodeposition coating of these coating compositions have a very rough, uneven surface texture and lack coating smoothness. And, since these coating compositions do not have any sufficient press-processability, either, the portions where these coating compositions can be applied are limited.

Further, Japanese Patent KOKOKU (Post-Exam. Publn.) No. Sho 60-33192, Japanese Patent KOKAI (Laid-Open) Nos. Sho 58-224174 and 60-174879, etc., propose organic composite silicate films and steel sheets coated with such a film, in which electrodeposition coating can be carried out to form thin films containing no electrically conductive pigment and having a thickness of 0.3 to 3 μm and steel sheets coated with these films. Although these organic composite silicate films and coated steel sheets have improved high corrosion resistance, weldability, press-processability, etc., they still have a problem in that an undercoat is seen through the films since the films are clear, or a handling problem in that the distinction between a coated surface and an uncoated surface is difficult when one surface of a steel sheet is coated. Furthermore, Japanese Patent KOKOKU (Post-Exam. Publn.) No. 55-5422, Japanese Patent KOKAI (Laid-Open) No. 58-61291, etc., describe colored precoat steel sheets of which the appearance design is improved by forming colored thick coating films having a thickness of 5 to 20 μm. Since, however, the films are thick and soft, these steel sheets have a defect in weldability and are liable to suffer scars in handling.

As described above, in fact, none of the conventionally proposed techniques have met the qualities presently required of a steel sheet coated with a colored thin film.

SUMMARY OF THE INVENTION

The object of this invention is to provide a colored plated steel sheet which permits not only welding but also press-processing and electrodeposition coating by coloring the surface of the plating of a plated steel sheet without losing the advantages of the plated steel sheet.

According to this invention, there is provided an organic composite steel sheet which comprises a substrate plated with zinc or a zinc-based alloy or a substrate plated with aluminum, a first layer of a sparingly soluble chromate film formed on the substrate and having a water soluble content of 1 to 30%, a Cr⁶⁺ /Cr³⁺ ratio of 0.01 to 1.0 and a total chromium built-up, on one surface, of 10 to 150 mg/m², and a second layer of a 0.3 to 5 μm-thick solid film formed of a solvent-type coating composition comprised of, based on the weight of the nonvolatile content, 5 to 40% by weight of a hydrophilic polyamide resin having a polymerization degree of 50 to 1,000, 5 to 40% by weight of a silica fine powder having an average particle diameter of 1 to 100 mμ, 1 to 20% by weight of a lubricant such as polyethylene wax, etc., having a molecular weight of 1,000 to 10,000, 0.1 to 20% by weight of at least one member selected, as a sparingly soluble pigment, from the group consisting of insoluble azo, azolake or phthalocyanine-type organic pigments and inorganic pigments having an average particle diameter of 0.05 to 5 μm, and 30 to 90% by weight of a urethanated epoxy ester resin as a binder.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

This invention seeks to overcome degradation of press-processability and corrosion resistance involved in the formation of a thin film and a "seeing-through" problem of a colored film due to a thin film by combining the modification of a coloring coating composition with an undercoating film.

As described above, this invention is featured by a combination of the sparingly soluble chromate coating film with the solid coating film formed of a solvent-type colored organic polymer resin prepared by compounding a highly water-resistant epoxy-based resin, a hydrophilic polyamide resin, a fine powder silica and a coloring pigment. And, this invention has been completed on the basis of the following findings: The hydrophilic polyamide resin is necessary for smoothness of an electrodeposited film (gas pinholes, craters and organe peel). The use of no fine powder silica deteriorates adherence and corrosion resistance. A combination of the hydrophilic polyamide resin with the fine silica powder, i.e. a combination of a soft resin with a high-hardness resin, gives a good effect on a film lubricity, but the highly corrosion-resistant binder is required due to insufficient electrodeposition with the electrodeposited film. A specific insoluble coloring pigment is necessary to uniformly form a colored appearance film through which no undercoating film is seen even if it is a thin film. The undercoat chromate film has to be sparingly soluble to improve the secondary adherence of the electrodeposited film for water resistance.

Examples of the steel sheet used in this invention include a zinc-electroplated steel sheet, steel sheet hot-dipped with zinc, steel sheet electroplated with a zinc alloy (Zn-Ni, Zn-Cr and Zn-Fe), steel sheet electroplated with a zinc-based composite (Zn-Ni-SiO₂, Zn-Ni-ZrO₂, Zn-Cr-SiO₂, Zn-Cr-ZrO₂, etc.), steel sheet hot dipped with a zinc-based alloy (Zn-Al, Zn-Mg and Zn-Ni), steel sheet hot dipped with aluminum, steel sheet plated with alloyed zinc and multilayered steel sheets of these platings.

It is essential to increase Cr³⁺ in the chromate film formed as a first layer on the plated steel sheet, in order to render the film sparingly soluble. As a method therefor there are a method of cathodic electrolysis in a chromating bath, and a coating-type chromating method in which Cr⁶⁺ is reduced in Cr³⁺ in the presence of an organic reducing agent such as saccharides or alcohols and the Cr⁶⁺ and Cr³⁺ are controlled in a suitable ratio. In this invention, either of these methods or a combination of these methods may be used. And, a colloidal silica (sol) may be incorporated.

The chromate film of this invention, obtained above, has a water soluble content (% chromium elution) of 1 to 30%, preferably 3 to 15%. The water soluble content of less than 1% is unsuitably short for the self-healing with Cr⁶⁺, and the corrosion resistance is consequently reduced. When it exceeds 30%, the film swells due to eluted chromium, and secondary adherence and a pH at interface in cationic electrodeposition coating are reduced. As a result, a hydrogen gas generation is liable to remain on the electrodeposited film appearance in a form of pinholes (gas pinholes) or orange peel, and the appearance and appearance smoothness are undesirably hampered. The ratio of Cr⁶⁺ /Cr³⁺ as components for the sparingly soluble chromate film of this invention is 0.01 to 1.0, preferably 0.03 to 0.5. When this ratio is less than 0.01, the achievement of high corrosion resistance is difficult due to insufficient self-healing effect with Cr⁶⁺ (soluble chromium), and when it exceeds 1.0, chromium (Cr⁶⁺) eluted into a treating liquid increases and builds up at an electrodeposition coating time or at a pretreatment time therefor such as alkali degreasing or treatment with a phosphate. Thus, the suitable bath balance of the treating liquid is hampered, which is undesirably a bar against the electrodeposition coatability including the treatment with a phosphate.

The build-up of the above sparingly soluble chromate film of this invention is 10 to 150 mg/m² (one surface) as a total chromium content, preferably 30 to 100 mg/m². When the total chromium content is less than 10 mg/m², the electrodeposition coating film does not exhibit adherence and high corrosion resistance as expected. And, when it is over 150 mg/m², various performances of the electrodeposition coating film such as adherence, press-processability, continuous spot-weldability, etc., are undesirably reduced.

The thin colored coating film as secondary layer is then formed on the chromate coating film. The requirements for this formation are as follows.

First, the urethanated epoxy ester resin as a binder is an epoxy-based binder resin which has a number average molecular weight of 300 to 100,000 and which is selected from the group consisting of an epoxy resin containing not less than 50% by weight, based on the weight of the nonvolatile content, of phenol in the molecule, an epoxy ester resin produced by reacting said epoxy resin with a dicarboxylic acid in the presence or absence of an amine catalyst and a urethanated epoxy ester resin produced by reacting said epoxy ester resin with a partial block isocyanate compound. The epoxy-based binder resin is used in an amount of 30 to 90% by weight based on the weight of the nonvolatile content. When the above number average molecular weight is less than 300, the adherence and corrosion resistance are reduced. And, a resin which can be used as a coating composition by dissolving it in an organic solvent have a molecular weight of up to 100,000, preferably 2,000 to 20,000.

When the amount of such an epoxy-based binder resin having a number average molecular weight in the above-specified range is less than 30% by weight based on the weight of the nonvolatile content, the adherence and processability of the resultant electrodeposition film are reduced. And, when it is over 90% by weight, the binder function for the coating composition decreases almost by half.

The hydrophilic polyamide resin used as a second resin component together with the above binder resin is one of the most important factors for the constitution of this invention, and featured by that it has many acid amide bonds and is highly hydrophilic and highly hygroscopic and that it has a high polymerization degree and a high molecular weight. In addition, the hydrophilic polyamide resin is selected from nylon 6 and nylon 6,6 or a copolymer of this nylon with some other nylon; polyether polyol-, polyester polyol-, or polybutadiene polyol-modified nylon; and aromatic polyamides such as poly-m-phenyleneisophthalamide, poly-p-phenyleneterephthalamide, etc. The present inventors have found that when such a hydrophilic polyamide resin is incorporated into a colored thin coating film, an electrodeposition liquid penetrates a coating film at an electrodeposition coating time, and electric resistance of the coating film is therefore lowered, whereby the electrodeposition property and electrodeposition coating film appearance (prevention of occurrence of gas pinholes, orange peel, etc.) are remarkably improved. This finding forms one of the essential bases for this invention. The large molecular weight of the polyamide resin is useful for prevention of the swelling and dissolving of a resin for the thin film-coated colored steel sheet in pretreatment procedures for electrodeposition coating, particularly at an alkali degreasing or electrodeposition coating time. That is, the polymerization degree is 50 to 1,000, preferably 50 to 500. When the polymerization degree is less than 50, the film undergoes dissolution at the above alkali degreasing time or electrodeposition time, and no uniform appearance is obtained. And, reduction of acid resistance occurs. The polymerization degree of over 1,000 is too high a molecular weight to meet the object of this invention. The incorporation of the polyamide resin is also desirable in view of impartation of flexibility and high processability into the coating film. The amount of the polyamide resin to be incorporated is 5 to 40% by weight, preferably 5 to 25% by weight based on the coating composition nonvolatile content. When this amount is less than 5% by weight, the uniform electrodeposition coating property (gas pin-holes or organce peel) is not improved as expected. And, when it exceeds 40% by weight, the adherence of the electrodeposition coating film is degraded.

In this invention, in order to improve corrosion resistance, a silica having an average particle diameter of 1 to 100 mμ, preferably 5 to 50 mμ is used in an amount of 5 to 40% by weight, preferably 10 to 20% by weight, based on the coating composition nonvolatile content. When particles of the silica have a primary particle diameter of less than 1 mμ, alkali resistance of the resultant composite coating film is undesirably low. And, when it is over 100 mμ, there is no effect on improvement in corrosion resistance, and the resultant electrodeposition coating film has poor smoothness. Examples of such silica particles are fumed silica, colloidal silica, etc. Above all, the fumed silica is preferably used. The colloidal silica contains ammonium and alkali metal ions to stabilize its colloid, and these ions tend to lower corrosion resistance function of the film. When the amount of the silica particles is less than 5% by weight, there is no effect on improvement in corrosion resistance. And, the amount of over 40% by weight shows reduction in processability, and does not achieve the object of this invention.

The application requirements of the coloring pigment to be used to color the coating composition of this invention are as follows.

Of a variety of coloring pigments, the coloring pigments applicable to the coating composition in this invention are basically required to be sparingly soluble in water, and sparingly soluble and uniformly dipersible in an organic solvent for the coating composition. If the coloring pigment is soluble, it is eluted into an alkali degreasing liquid and a phosphate treatment liquid during the pretreatment for cationic electrodeposition coating even after it is solidified as a coating film. And, as result, the colored coating film undergoes color fading to a great extent, and it is also included in such treating liquids. Hence, the soluble coloring pigment is not practical. Further, when cationic electrodeposition coating or overcoating is effected thereon, the coloring pigment in the colored coating film is eluted, a color is transferred to the cationic electrodeposition coating film, and the coloring pigment is released into the overcoating film to cause a problem on bleeding resistance, etc. Therefore, the soluble coloring pigment is excluded from the scope of this invention.

Therefore, the requirements of the coloring pigment usable in the coating composition of this invention are that it should be sparingly soluble or insoluble in the solvent for the coating composition, and uniformly dispersible therein. Examples of the coloring pigment meeting such requirements are insoluble azo-, azolake- and phthalocyanine-type organic pigments or ordinary insoluble inorganic pigments.

When the coloring pigment has an average particle diameter of less than 0.05 μm, it undergoes secondary aggregation in the coating composition to form coarse particles, and the uniform coloring of the resultant coating film appearance is deteriorated. The average particle diameter of over 5 μm is not very desirable in view of coating film smoothness finish. For this reason, the average particle diameter of the coloring pigment is preferably 0.1 to 2.0 μm.

Further, when the amount of the coloring pigment incorporated into the coating composition of this invention is less than 0.1% by weight based on the coating composition nonvolatile content, the pigmentation degree of the resultant coating film is low, and the effects on the pigmentation degree for the design and the distinction of a coated surface by the eyes intended by this invention are small. And, when it is over 20% by weight, impractically, the effect of the pigment binder as said main resin is lost, and the uniform coatability of the resultant coating composition is reduced. The amount of the coloring pigment is preferably 0.3 to 10% by weight based on the coating composition nonvolatile content.

As described above, the thin colored coating film of this invention contains, as a nonvolatile content, the specified amounts of the epoxy-based binder resin, the hydrophilic polyamide resin, the fine powder silica and the insoluble coloring pigment. And, the combination of these four components synergistically improves electrodepsotion coatability, and gives a colored coating film having high corrosion resistance, high processability, excellent adherence, excellent smoothness and spot-weldability.

In addition, it is desirable to incorporate 1 to 20% by weight, preferably 1 to 10% by weight, based on the coating composition nonvolatile content, of a lubricant such as a polyolefin, a carboxylate, a metal carboxylate, a polyalkylene glycol or the like, or a lubricant powder such as molybdenum disulfide, a silicone compound, a fluorine compound or the like into the coating composition of this invention thereby to further improve the processability. A particularly preferable lubricant is a polyethylene wax having a molecular weight of 1,000 to 10,000. When the lubricant is incorporated, however, the amount thereof is up to 20% by weight at maximum. If the amount exceeds this limit, the adherence of the resultant electrodeposition film is undesirably reduced.

Further, in order to impart the coating composition of this invention with a low-temperature baking function, the coating composition can be thermoset by incorporating a curing agent such as a melamine resin, resol-type phenolic resin, polyisocyanate, or the like in a curing agent/epoxy resin ratio of 0.1/9.9 to 4/6 as solid contents by weight. The resol-type phenolic resin represented by the following formula is particularly preferable. ##STR1## wherein n is 0 to 4, W is --CH₂ -- or --CH₂ --O-CH₂ --, and R is CH₃, H or --C(CH₃)₂ OH.

The coating composition for a thin colored coating film of this invention may be coated on the coated steel sheet by a roll coat method, spray method, shower coat method, or the like, and the baking sheet temperature is 100 to 250° C. The dried coating film thickness is 0.3 to 5 μm, preferably 0.5 to 3 μm. When this thickness is less than 0.3 μm, the uniform colored coatability, corrosion resistance, press lubricity, etc., are reduced. And, when it is over 5 μm, the spot-weldability cannot be obtained stably as expected.

This invention will be illustrated by reference to Examples, in which % stands for % by weight based on the weight of the nonvolatile content of the coating composition unless otherwise specified.

The chromate film as first layer was formed on a steel sheet prepared by plating the surface of a low-carbon steel sheet having a thickness of 0.8 mm and a width of 1,000 mm with zinc or a zinc alloy given in Table 1. That is, the chromate film formation was carried out by a cathodic electrolytic method using a chromating liquid containing 3 to 10 g/l of alcohol-reduced Cr³⁺ at a bath temperature of 45° C. at a current density of 15 A/dm³ and/or a method of coating the surface with the chromating liquid. Then, as a second layer, an organic solvent-type colored coating composition comprised of given components was roll-coated thereon such that the resultant solid coating film had a thickness of 0.3 to 5 μm. And, the coated steel sheet was baked at a final sheet temperature of 150° C., cooled with water and dried.

In Table 1, examples of this invention for coated steel sheets prepared according to the above procedures are indicated as Nos. 1 to 78, and Comparative Examples as Nos. 79 to 106.

First, concerning the function and effect of the chromate film as a first layer on specific factors, Examples of this invention are shown in Nos. 1 to 19, and Comparative Examples in Nos. 79 to 84. These results show that it is essential to render the chromate film sparingly insoluble in order to allow the chromate film as an interlayer between a plating layer and an upper colored thin coating film to exhibit high-level total performances of a colored organic composite plated steel sheet such as corrosion resistance, adherence, etc., and that the Cr⁶⁺ /Cr³⁺ amount in the chromate film and the build-up of the chromate film have to be adjusted to the ranges specified in this invention.

Secondary, concerning the function and effect of the specific factors constituting the colored coating film as second layer, Examples of this invention are shown in Nos. 20 to 72, and Comparative Examples in Nos. 85 to 106. Of these Examples, the function and effect of this invention concerning the molecular weight range and composition ratio of the binder resin are shown in No. 4 and Nos. 20 to 27, and those of Comparative Examples in Nos. 85 to 88.

These results clearly show that the suitable molecular weight and composition ratio specified in this invention are required to allow the pigment contained in a coating composition to exhibit the specified performances by dispersing it in a coating film.

Further, it is necessary to use the hydrophilic polyamide resin specified in this invention in combination in order to obtain excellent electrodeposition coatability by decreasing an electrodeposition interface resistance at an electrodeposition coating time. Examples of this invention therefor are shown in No. 4 and Nos. 28 to 35, and Comparative Examples in Nos. 89 to 92. These results clearly show that the hydrophilic polyamide resin has a great effect to balance the electrodeposition coatability and the other performances at an excellent level, and that the polymerization degree and composition ratio thereof are required to come under the ranges specified by this invention.

And, fumed silica is an essential factor to impart a colored organic composite plated steel sheet with high corrosion resistance. Comparative data on this point between this invention and Comparative Examples are shown in Nos. 4 and 36 to 45 and in Nos. 93 to 96. These results clearly show that, in order to achieve high corrosion resistance well-balanced with the other performances, it is necessary to select the fumed silica such that its particle diameter and composition ratio come within the ranges specified by this invention.

Furthermore, a wax is necessary to obtain excellent lubricity and press-processability. Examples of this invention using a polyethylene wax are shown in Nos. 46 to 53, and Comparative Examples in Nos. 97 to 100. These results show that the molecular weight and composition ratio of the polyethylene wax are required to come within the ranges specified in this invention.

The coloring pigment is used to color the coating composition of this invention. Examples of this invention for the coloring pigment are shown in Nos. 54 to 66 and 4, and Comparative Examples therefor in Nos. 103 to 106. These results show that any organic or inorganic coloring pigments are usable in this invention without any problem on performance if they are insoluble, and that the particle diameter and composition ratio thereof should come within the ranges specified in this invention in view of smoothness and uniform finish of colored appearance.

Examples of this invention for suitable thicknesses of the colored coating films are shown in Nos. 4 and 67 to 72, and Comparative Examples for such thickness in Nos. 101 and 102. These results show that the thickness lower limit should come within the range specified in this invention in view of uniformity of colored appearance, press-processability and corrosion resistance, and that the thickness upper limit also should come within the range specified in this invention in view of spot-weldability.

In addition, examples of plated steel sheets to which this invention can be applied are shown in Nos. 4 and 73 to 78, and the results show that this invention can be applied to all of these plated sheets.

    TABLE 1       Colored organic composite coating film (second layer)  Chromate Binder       Plated film resin *2 Hydrophilic Fumed steel sheet (first layer) *1      Number average  resin *3 silica *4   Kind of Build-up of Build-up  Water      soluble molecular  Polymerization  Average particle   No. plating      plating g/m.sup.2 mg/m.sup.2 Cr.sup.6+ /Cr.sup.3+  ratio content (%)      weight Amount wt % degree Amount wt % diameter (μm) Amount wt      %         This 1 Galvanized 20 50 0.01 10 1 × 10.sup.4 60 300 20 8 1      5 invention  Zn--Ni   (Ni 11%) This 2 Galvanized 20 50 0.0310 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 3 Galvanized      20 50 0.05 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 4 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 5 Galvanized 20 50 0.3 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 6 Galvanized      20 50 0.5 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 7 Galvanized 20 50 1.0 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 8 Galvanized 20 50 0.1 1 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 9 Galvanized      20 50 0.1 3 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 10 Galvanized 20 50 0.1 5 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 11 Galvanized 20 50 0.1 15 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 12 Galvanized      20 50 0.1 20 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 13 Galvanized 20 50 0.1 30 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 14 Galvanized 20 10 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 15 Galvanized      20 30 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 16 Galvanized 20 70 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 17 Galvanized 20 100 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 18 Galvanized      20 120 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 19 Galvanized 20 150 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 20 Galvanized 20 50 0.1 10 3 ×      10.sup.2 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 21 Galvanized      20 50 0.1 10 3 × 10.sup.3 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 22 Galvanized 20 50 0.1 10 3 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 23 Galvanized 20 50 0.1 10 10 ×      10.sup.4  60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 24 Galvanized      20 50 0.1 10 1 × 10.sup.4 30 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 25 Galvanized 20 50 0.1 10 1 × 10.sup.4 40 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 26 Galvanized 20 50 0.1 10 1 ×      10.sup.4 80 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 27 Galvanized      20 50 0.1 10 1 × 10.sup.4 90 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 28 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 50 20 8 15      invention  Zn--Ni   (Ni 11%) This 29 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 10020 8 15 invention  Zn--Ni   (Ni 11%) This 30 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 500 20 8 15 invention  Zn--Ni   (Ni      11%) This 31 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 1000 20 8 15      invention  Zn--Ni   (Ni 11%) This 32 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 5 8 15 invention  Zn--Ni   (Ni 11%) This 33 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 10 8 15 invention  Zn--Ni   (Ni      11%) This 34 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 25 8 15      invention  Zn--Ni   (Ni 11%) This 35 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 40 8 15 invention  Zn--Ni   (Ni 11%) This 36 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 1 15 invention Zn--Ni   (Ni      11%) This 37 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 5 15      invention Zn--Ni   (Ni 11%) This 38 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 10 15 invention Zn--Ni   (Ni 11%) This 39 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 50 15 invention Zn--Ni   (Ni      11%) This 40 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 100 15      invention Zn--Ni   (Ni 11%) This 41 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 5 invention Zn--Ni   (Ni 11%) This 42 Galvanized 20      50 0.1 10 1 × 10.sup.4 60 300 20 8 10 invention Zn--Ni   (Ni 11%)      This 43 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention Zn--Ni   (Ni 11%) This 44 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 20 invention Zn--Ni   (Ni 11%) This 45 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 40 invention Zn--Ni   (Ni      11%) This 46 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention Zn--Ni   (Ni 11%) This 47 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention Zn--Ni   (Ni 11%) This 48 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention Zn--Ni   (Ni      11%) This 49 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention Zn--Ni   (Ni 11%) This 50 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 51 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 52 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 53 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 54 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 55 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 56 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 57 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 58 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 59 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 60 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 61 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 62 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 63 Galvanized      20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 64 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 65 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 66 Galvanized      20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 67 Galvanized 20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 68 Galvanized 20 5 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 69 Galvanized      20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 70 Galvanized 20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn--Ni   (Ni 11%) This 71 Galvanized 20 5 0.1 10 1 ×      10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni 11%) This 72 Galvanized      20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Ni   (Ni      11%) This 73 Galvanized 20 5 0.1 10 1 × 10.sup.4 60 300 20 8 15      invention  Zn This 74 Galvanized 20 5 0.1 10 1 × 10.sup.4 60 300      20 8 15 invention  Zn--Fe   (Fe 80%) This 75 Hot Dipped 100 5 0.1 10 1      × 10.sup.4 60 300 20 8 15 invention  Zn This 76 Hot Dipped 45 5      0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn-- Fe This 77 Hot      Dipped 100 5 0.1 10 1 × 10.sup.4 60 300 20 8 15 invention  Zn--Al       (Al 5%) This 78 Hot Dipped 100 5 0.1 10 1 × 10.sup.4 60 300 20 8      15 invention  Al Comparative 79 Galvanized 20 5 0.1 10 1 ×      10.sup.4 60 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 80      Galvanized 20 180 0.1 10 1 × 10.sup.4 60 300 20 8 15 Example      Zn--Ni   (Ni 11%) Comparative 81 Galvanized 20 50 0.008 10 1 ×      10.sup.4 60 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 82      Galvanized 20 50 1.2 10 1 × 10.sup.4 60 300 20 8 15 Example      Zn--Ni   (Ni 11%) Comparative 83 Galvanized 20 50 0.1 0.5 1 ×      10.sup.4 60 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 84      Galvanized 20 50 0.1 35 1 × 10.sup.4 60 300 20 8 15 Example      Zn--Ni   (Ni 11%) Comparative 85 Galvanized 20 50 0.1 10 2 ×      10.sup.2 60 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 86      Galvanized 2050 0.1 10 11 × 10.sup.4   60 300 20 8 15 Example      Zn--Ni   (Ni 11%) Comparative 87 Galvanized 2050 0.1 10 1 ×      10.sup.4 20 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 88      Galvanized 2050 0.1 10 1 × 10.sup.4 95 300 20 8 15 Example  Zn--Ni        (Ni 11%) Comparative 89 Galvanized 2050 0.1 10 1 × 10.sup.4 60      30 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 90 Galvanized 2050 0.1      10 1 × 10.sup.4 60 1500 20 8 15 Example  Zn--Ni   (Ni 11%)      Comparative 91 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 3 8 15      Example  Zn--Ni   (Ni 11%) Comparative 92 Galvanized 20 50 0.1 10 1      × 10.sup.4 60 300 45 8 15 Example  Zn--Ni   (Ni 11%) Comparative      93 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 0.5 15 Example      Zn--Ni   (Ni 11%) Comparative 94 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 150 15 Example  Zn--Ni   (Ni 11%) Comparative 95      Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 3 Example  Zn--Ni        (Ni 11%) Comparative 96 Galvanized 20 50 0.1 10 1 × 10.sup.4 60      300 20 8 5.0 Example  Zn--Ni   (Ni 11%) Comparative 97 Galvanized 20 50      0.1 10 1 × 10.sup.4 60 300 20 8 1.5 Example  Zn--Ni   (Ni 11%)      Comparative 98 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8      1.5 Example  Zn--Ni   (Ni 11%) Comparative 99 Galvanized 20 50 0.1 10 1      × 10.sup.4 60 300 20 8 1.5 Example  Zn--Ni   (Ni 11%) Comparative      100 Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 1.5 Example      Zn--Ni   (Ni 11%) Comparative 101 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 1.5 Example  Zn--Ni   (Ni 11%) Comparative 102      Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 1.5 Example      Zn--Ni   (Ni 11%) Comparative 103 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 1.5 Example  Zn--Ni   (Ni 11%) Comparative 104      Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 Example      Zn--Ni   (Ni 11%) Comparative 105 Galvanized 20 50 0.1 10 1 ×      10.sup.4 60 300 20 8 15 Example  Zn--Ni   (Ni 11%) Comparative 106      Galvanized 20 50 0.1 10 1 × 10.sup.4 60 300 20 8 15 Example      Zn--Ni   (Ni 11%)        Cationic electrode position (Power Top U100) Poly-    Electrode-      Adherence of ethylene Coloring   position electrode- wax *5 pigment *6      Alkali-resistance appearance *10 position Molecular Amount  Average      particle Amount Coating film  Coloring uniformity swelling of coating      Gas  coating film *11  No. weight wt % Type diameter (μm) wt %      thickness *7 of appearance *8 film *9 pinhole Crater Orange peel Primary S      econdary        This 1 3 ×       10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚ .circleincirc      le. ⊚ ⊚ ⊚ ⊚      invention This 2 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 3 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 4 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 5 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 6 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 7 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 8 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 9 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 10 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 11 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 12 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 13 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 14 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 15 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 16 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 17 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 18 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 19 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 20 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 21 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 22 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 23 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 24 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 25 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 26 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 27 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 28 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 29 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 30 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 31 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 32 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 33 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 34 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 35 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 36 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 37 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 38 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 39 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 40 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 41 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 42 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 43 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 44 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 45 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 46 1 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 47 5 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 48 1 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 49 3 × 10.sup.3 1      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 50 3 × 10.sup.3 3 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚  ⊚      ⊚ ⊚ invention This 51 3 × 10.sup.3 7      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 52 3 × 10.sup.3 10 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 53 3 × 10.sup.3      20 D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 54 3 × 10.sup.3 5 D 0.05 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 55 3 × 10.sup.3 5      D 1.0 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 56 3 × 10.sup.3 5 D 2.0 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 57 3 × 10.sup.3 5      D 5.0 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 58 3 × 10.sup.3 5 D 0.2 0.1 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 59 3 × 10.sup.3 5      D 0.2 0.3 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 60 3 × 10.sup.3 5 D 0.2 5.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 61 3 × 10.sup.3 5      D 0.2 10.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 62 3 × 10.sup.3 5 D 0.2 20.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 63 3 × 10.sup.3 5      E 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 64 3 × 10.sup.3 5 A 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 65 3 × 10.sup.3 5      B 0.2 2.0 1.0⊚ ⊚  ⊚      ⊚ ⊚ ⊚ ⊚      invention This 66 3 × 10.sup.3 5 C 0.2 2.0 1.0⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 67 3 × 10.sup.3 5      D 0.2 2.0 0.3⊚ ⊚ ⊚ .circlein      circle. ⊚ ⊚ ⊚ invention      This 68 3 ×       10.sup.3 5 D 0.2 2.0 0.5⊚ ⊚ .circleincircl      e. ⊚ ⊚ ⊚ ⊚      invention This 69 3 × 10.sup.3 5 D 0.2 2.0 0.8⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 70 3 × 10.sup.3 5      D 0.2 2.0 1.5⊚ ⊚ ⊚ .circlein      circle. ⊚ ⊚ ⊚ invention      This 71 3 ×       10.sup.3 5 D 0.2 2.0 2.0⊚ ⊚ .circleincircl      e. ⊚ ⊚ ⊚ ⊚      invention This 72 3 × 10.sup.3 5 D 0.2 2.0 5.0⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 73 3 × 10.sup. 3      5 D 0.2 2.0 1.0⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention This 74 3 × 10.sup.3 5 D 0.2 2.0 1.0⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 75 3 × 10.sup.3 5      D 0.2 2.0 1.0⊚ ⊚ ⊚ .circlein      circle. ⊚ ⊚ ⊚ invention      This 76 3 ×       10.sup.3 5 D 0.2 2.0 1.0⊚ ⊚ .circleincircl      e. ⊚ ⊚ ⊚ ⊚      invention This 77 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ invention This 78 3 × 10.sup.3 5      D 0.2 2.0 1.0 ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      invention Comparative 79 3 ×       10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚ .circleincirc      le. ⊚ ⊚ ◯ ◯-Δ       Example Comparative 80 3 ×       10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚ ◯      -Δ  ◯-Δ ⊚ ◯ .largecirc      le.-Δ Example Comparative 81 3 × 10.sup.3 5 D 0.2 2.0 1.0      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ Example Comparative      82 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚      Δ Δ ◯ ⊚-◯ .largecircle      .-Δ Example Comparative 83 3 × 10.sup.3 5 D 0.2 2.0 1.0      ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ Example Comparative      84 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚      Δ-X Δ-X ◯ ⊚ ◯-Δ      Example Comparative 85 3 ×       10.sup.3 5 D 0.2 2.0 1.0 ⊚ Δ-X ⊚      ⊚ Δ-X ⊚ ◯ Example      Comparative 86 3 × 10.sup.3 5 D 0.2 2.0 1.0 X (Unsuitable as a      coating composition) Example Comparative 87 3 × 10.sup.3 5 D  0.2      2.0 1.0 ⊚ ⊚ ⊚ .circleincircl      e. ⊚ Δ Δ-X Example Comparative 88 3 ×      10.sup.3 5 D 0.2 2.0 1.0 X (Unsuitable as a coating composition) Example C      omparative 89 3 × 10.sup.3 5 D 0.2 2.0 1.0 ⊚ X      ⊚ ⊚ X ◯ Δ-X Example      Comparative 90 3 × 10.sup.3 5 D 0.2 2.0 1.0 X (Unsuitable as a      coating composition) Example Comparative 91 3 × 10.sup.3 5 D 0.2      2.0 1.0 ⊚ ⊚ X X ⊚ .circleinc      ircle. ⊚ Example Comparative 92 3 × 10.sup.3 5 D      0.2 2.0 1.0 ⊚ ⊚ ⊚ .circleinc      ircle. ⊚ Δ Δ-X Example Comparative 93 3      ×  10.sup.3 5 D 0.2 2.0 1.0 ⊚ ⊚      ◯ ◯ ◯ ⊚ .circleincircl      e. Example Comparative 94 3 × 10.sup.3 5 D 0.2 2.0 1.0 Δ-X      ⊚ ◯ ◯ Δ ⊚      ⊚ Example Comparative 95 3 × 10.sup.3 5 D 0.2 2.0      1.0 ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ Example Comparative      96 3 ×       10.sup.3 5 D 0.2 2.0 1.0 Δ ⊚ ⊚      ⊚ ⊚ ⊚ ⊚      Example Comparative 97 500 5 D 0.2 2.0 1.0 ⊚ .circleincirc      le. ⊚ ⊚ ⊚ ⊚      ⊚ Example Comparative 98 2 × 10.sup.4 5 D 0.2 2.0      1.0 ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ Example Comparative      99 3 ×       10.sup.3 0.5 D 0.2 2.0 1.0 ⊚ ⊚ .circleinci      rcle. ⊚ ⊚ ⊚ ⊚       Example Comparative 100 3 ×       10.sup.3 30 D 0.2 2.0 1.0 ⊚ ⊚ .circleincir      cle. ⊚  ⊚ ◯ Δ Example      Comparative 101 3 × 10.sup.3 5 D 0.2 2.0 1.0 X ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ Example Comparative 102 3 × 10.sup.3 5 D 0.2 2.0      1.0 ⊚ ⊚ ⊚ ⊚      ⊚ ⊚ ⊚ Example Comparative      103 3 × 10.sup.3 5 D 0.02 2.0 1.0 Δ ⊚      ⊚ ⊚ ⊚ ⊚      ⊚ Example Comparative 104 3 × 10.sup.3 5 D 10 2.0      1.0 Δ-X ⊚ ◯ ◯ ◯      ⊚ ⊚ Example Comparative 105 3 ×      10.sup.3 5 D 0.2 0.05 1.0 ◯ ⊚ ⊚       ⊚ ⊚ ⊚ ⊚      Example Comparative 106 3 × 10.sup.3 5 D 0.2 30 1.0 X (Unsuitable      as a coating composition) Example        Press-   processability *12 Corrosion Capability in  No. Galling      Powdering resistance *13 numbers of weld *14        This 1 ⊚ ⊚ ⊚ .circleincirc      le. invention This 2 ⊚ ⊚ ⊚      ⊚ invention This 3 ⊚ ⊚      ⊚ ⊚ invention This 4 ⊚      ⊚ ⊚ ⊚ invention This 5      ⊚ ⊚ ⊚ ⊚      invention This 6 ⊚ ⊚ ⊚      ⊚ invention This 7 ⊚ ⊚      ⊚ ⊚ invention This 8 ⊚      ⊚ ⊚ ⊚ invention This 9      ⊚ ⊚ ⊚ ⊚      invention This 10 ⊚ ⊚ ⊚      ⊚ invention This 11 ⊚ ⊚      ⊚ ⊚ invention This 12 ⊚      ⊚ ⊚ ⊚ invention This 13      ⊚ ⊚ ⊚ ⊚      invention This 14 ⊚ ⊚ ⊚      ⊚ invention This 15 ⊚ ⊚      ⊚ ⊚ invention This 16 ⊚      ⊚ ⊚ ⊚ invention This 17      ⊚ ⊚ ⊚ ⊚      invention This 18 ⊚ ⊚ ⊚      ⊚ invention This 19 ⊚ ⊚      ⊚ ⊚ invention This 20 ⊚      ⊚ ⊚ ⊚ invention This 21      ⊚ ⊚ ⊚ ⊚      invention This 22 ⊚ ⊚ ⊚      ⊚ invention This 23 ⊚ ⊚      ⊚ ⊚ invention This 24 ⊚      ⊚ ⊚ ⊚ invention This 25      ⊚ ⊚ ⊚ ⊚      invention This 26 ⊚ ⊚ ⊚      ⊚ invention This 27 ⊚ ⊚      ⊚ ⊚ invention This 28 ⊚      ⊚ ⊚ ⊚ invention This 29      ⊚ ⊚ ⊚ ⊚      invention This 30 ⊚ ⊚ ⊚      ⊚ invention This 31 ⊚ ⊚      ⊚ ⊚ invention This 32 ⊚      ⊚ ⊚ ⊚ invention This 33      ⊚ ⊚ ⊚ ⊚      invention This 34 ⊚ ⊚ ⊚      ⊚ invention This 35 ⊚ ⊚      ⊚ ⊚ invention This 36 ⊚      ⊚ ⊚ ⊚ invention This 37      ⊚ ⊚ ⊚ ⊚      invention This 38 ⊚ ⊚ ⊚      ⊚ invention This 39 ⊚ ⊚      ⊚ ⊚ invention This 40 ⊚      ⊚ ⊚ ⊚ invention This 41      ⊚ ⊚ ⊚ ⊚      invention This 42 ⊚ ⊚ ⊚      ⊚ invention This 43 ⊚ ⊚      ⊚ ⊚ invention This 44 ⊚      ⊚ ⊚ ⊚ invention This 45      ⊚ ⊚ ⊚ ⊚      invention This 46 ⊚ ⊚ ⊚      ⊚ invention This 47 ⊚ ⊚      ⊚ ⊚ invention This 48 ⊚      ⊚ ⊚ ⊚ invention This 49      ⊚ ⊚ ⊚ ⊚      invention This 50 ⊚ ⊚ ⊚      ⊚ invention This 51 ⊚ ⊚      ⊚ ⊚ invention This 52 ⊚      ⊚ ⊚ ⊚ invention This 53      ⊚ ⊚ ⊚ ⊚      invention This 54 ⊚ ⊚ ⊚      ⊚ invention This 55 ⊚ ⊚      ⊚ ⊚ invention This 56 ⊚      ⊚ ⊚ ⊚ invention This 57      ⊚ ⊚ ⊚ ⊚      invention This 58 ⊚ ⊚ ⊚      ⊚ invention This 59 ⊚ ⊚      ⊚ ⊚ invention This 60 ⊚      ⊚ ⊚ ⊚ invention This 61      ⊚ ⊚ ⊚ ⊚      invention This 62 ⊚ ⊚ ⊚      ⊚ invention This 63 ⊚ ⊚      ⊚ ⊚ invention This 64 ⊚      ⊚ ⊚ ⊚ invention This 65      ⊚ ⊚ ⊚ ⊚      invention This 66 ⊚ ⊚ ⊚      ⊚ invention This 67 ⊚ ⊚      ⊚ ⊚ invention This 68 ⊚      ⊚ ⊚ ⊚ invention This 69      ⊚ ⊚ ⊚ ⊚      invention This 70 ⊚ ⊚ ⊚      ⊚ invention This 71 ⊚ ⊚      ⊚ ⊚ invention This 72 ⊚      ⊚ ⊚ ⊚ invention This 73      ⊚ ⊚ ⊚ ⊚      invention This 74 ⊚ ⊚ ⊚      ⊚ invention This 75 ⊚ ⊚      ⊚ ⊚ invention This 76 ⊚      ⊚ ⊚ ⊚ invention This 77      ⊚ ⊚ ⊚ ⊚      invention This 78 ⊚ ⊚ ⊚      ⊚ invention Comparative 79 ◯ ◯-.DE      LTA. Δ ⊚ Example Comparative 80 ◯      Δ ⊚ ◯-Δ Example Comparative 81      ⊚ ⊚ Δ ⊚ Example      Comparative 82 ⊚ ⊚ ⊚      ⊚ Example Comparative 83 ⊚ ⊚       Δ-X ⊚ Example Comparative 84 ⊚      ⊚ ⊚ ⊚ Example Comparative      85 ⊚ ⊚ Δ ⊚ Example      Comparative 86 Example Comparative 87 ◯ Δ ◯       ⊚ Example Comparative 88 Example Comparative 89 Δ      Δ-◯  ⊚ Example Comparative 90 Example      Comparative 91 ⊚ ⊚ ⊚      ⊚ Example Comparative 92 ⊚ ⊚       ⊚ ⊚ Example Comparative 93 .circleincircle      . ⊚ X ⊚ Example Comparative 94 .largecircle      . ◯ Δ-X ⊚ Example Comparative 95      ⊚⊚X ⊚ Example Comparative      96 Δ Δ-X ⊚⊚ Example Comparative       97 ◯ ◯ ◯ ⊚ Example      Comparative 98 ◯-Δ ◯-Δ ◯      ⊚ Example Comparative 99 X X Δ ⊚      Example Comparative 100 ⊚⊚⊚.      circleincircle. Example Comparative 101 Δ Δ-X X .circleincirc      le. Example Comparative 102 ⊚⊚.circleincirc      le.X Example Comparative 103 ⊚⊚.circleincir      cle.⊚ Example Comparative 104 ⊚.circleincir      cle.◯ ⊚ Example Comparative 105 .circleincircl      e.⊚⊚⊚ Example Comparative      106 Example        (Notes) *1: A ratio between the build-up of chromium eluted after      immersion of one test piece in boiling water for 5 minutes and the      initial chromium build-up of the same test piece was indicated as a      water soluble content (%). The build up of chromium was converted as      metal chromium. *2: A mixture prepared by mixing a urethanated epoxy      ester resin (supplied by Nippon Paint Co., Ltd.) with a resol-type      phenolic resin (BKS-316, supplied by Showa Kobunshi K.K.) in a mixing      ratio of 8/2 was used. *3: Polypropylene glycol-modified nylon 6      (supplied by Toyo Rayon Co., Ltd.) was used. *4: Aerosil 300 (supplied      by Nippon Silica K.K.) *5: Selidust 3620 (supplied by Hoechst Japan), a      molecular weight 2,000. *6: Type A: Insoluble azo-type (Permanent Red      F5R), B: Insoluble azolake-type (alizarin lake), C: Phthalocyanine-type      (copper phthalocyanine), D: Red iron oxide (Fe.sub.2 O.sub.3), E:      Titanium white (TiO.sub.2) *7: Calculated according to a gravimetric      method. *8: Colored appearance (examined by the eyes) ⊚:      Smooth and uniformly colored, ◯: Smooth and uniformly      colored with slight clearness, Δ: Somewhat rough but colored      uniformly, X: Rough and colored nonuniformly *9: Alkali defatting 2%      SURFCLEANER (supplied by Nippon Paint Co., Ltd.), 65° C.,      immersed for 5 minutes. ⊚: No failure, ◯:      Slightly whitened, Δ: Partly whitened, X: Partially peeled *10:      Power Top U-100 (supplied by Nippon Paint Co., Ltd.), 250 V, 3 min., 20      μm, 28°       C. (Gas pinhole, crater) ⊚: No occurence, ◯:      A few points, Δ: Less than 10 points, X: Not less than 10 points      (Orange peel) ⊚: Smooth, ◯: Slightly occurred,       Δ: Partly occurred, X: Totally occurred *11: The secondary      adherence was determined by immersing a test piece in warm water at      40° C. for 7 days, cross-cutting its coated surface and peeling      with an adhesive tape. (2 Mm × 100 cross cuts) ⊚:      100/100, ◯: More than 95/100, Δ: Not less than 90/100,      X: Less than 90/100 *12: Cylindrical press, 80 in diameter × 50 in      height, without any lubricating oil (Galling) ⊚: No      occurrence, ◯: Slightly occurred, Δ: Partly occurred,      X: Totally occurred (Powdering) Processed portion taping ⊚      : No peel, ◯: Slightly occurred, Δ: Partly occurred,      X: Totally occurred *13: Cylindrical press (80 in diameter × 50 in      height), salt water spray test on processed portion (JIS Z-2371)      ⊚: Not more than 1% white rust, ◯: Not more      than 5% white rust, Δ: Not more than 10% white rust, X: Over 10%      rust occurrence *14: Electrode terminal diameter 6 mm Pressure: 200 kg      · f, Current: 9 KA, Time: Not more than 10 cycles ×      2,000, Sheet combination: Interior-exterior (Coated on one surface)      ⊚: Not less than 5,000 weld spots, ◯: Not      less than 4,000 weld spots, Δ: Not more than 3,000 weld spots, X:      Not more than 2,000 weld spots

As described above, the colored organic composite plated steel sheet of this invention is improved by coloring to make it possible to distinguish its coated surface by the eyes when it is handled particularly in press-processing, etc. And, the performance level belonging inherently to the steel sheet does not change at all even if it is colored, and high improvement in the added value of coated steel sheets for household appliances and automobile use are achieved. Further, the color tone, etc., can be adjusted within the scope of this invention, whereby the coated steel sheet can be fully used as a colored coated steel sheet in the field of household appliances. 

What is claimed is:
 1. A highly corrosion-resistant, colored thin film-coated steel sheet having excellent press-processability and spot-weldability, which comprises a plated steel sheet, a first layer of a sparingly soluble chromate film formed on at least one surface of the plated steel sheet said chromate film having a water soluble content of 1 to 30%, a Cr⁶⁺ /Cr³⁺ ratio of 0.01 to 1.0 and a total chromium build-up of 10 to 150 mg/m² on one surface, and a second layer of a 0.3 to 5 μm-thick solid coating film formed of an organic solvent coating composition comprises of, based on the weight of the nonvolatile content:(a) a urethanated epoxy ester resin having a number average molecular weight of 300 to 100,000; 30 to 90%, (b) a hydrophilic polyamide resin having a polymerization degree of 50 to 1,000: 5 to 40%, (c) a silica powder having an average particle diameter of 1 to 100 mμ: 5 to 40%, (d) a lubricant: 1 to 20%, and (e) at least one member selected from the group consisting of inorganic, and insoluble azo, azolake or phthalocyanine organic pigments having an average particle diameter of 0.05 to 5 μm: 0.1 to 20%.
 2. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the plated steel sheet is one member from the group consisting of a steel sheet electroplated with zinc, a steel sheet hot-dipped with zinc, a steel sheet electroplated with a zinc-based composite, a steel sheet hot dipped with aluminum, a steel sheet plated with alloyed zinc, and a steel sheet plated with a composite of these.
 3. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the total chromium build-up is 30 to 100 mg/m².
 4. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the urethanated epoxy ester resin is selected from the group consisting of an epoxy resin containing not less than 50% by weight, based on the nonvolatile content, of phenol in the molecule, an epoxy ester resin produced by reacting said epoxy resin with a dicarboxylic acid in the presence or absence of an amine catalyst and a urethanated epoxy ester resin produced by reacting said epoxy ester resin with a partial block isocyanate compound.
 5. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the urethanated epoxy ester resin has a number average molecular weight of 2,000 to 20,000.
 6. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the hydrophilic polyamide resin is selected from the group consisting of nylon 6, nylon 6,6,- a copolymer thereof with some other nylon; polyether polyol-, polyesterpolyol - and polybutadiene polyol-modified nylon; and aromatic polyamides.
 7. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the silica powder has an average particle diameter of 5 to 50 mμ.
 8. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the coloring pigment has an average particle diameter of 0.1 to 2.0 μm.
 9. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the lubricant is selected from the group consisting of polyolefins, carboxylates, a metal carboxylate, a polyalkylene glycol, molybdenum disulfide, a silicone compound and a fluorine compound.
 10. A highly corrosion-resistant, colored thin film-coated steel sheet according to claim 1, wherein the lubricant is a polyethylene wax having a molecular weight of 1,000 to 10,000.
 11. The highly corrosion-resistant, colored thin film-coated steel sheet according to claim 2 wherein said plated steel sheet is selected from the group consisting of steel sheet electroplated with a zinc alloy, and steel sheet hot-dipped with zinc alloy.
 12. The highly corrosion-resistant, colored thin film-coated steel sheet according to claim 2 wherein said plated steel sheet is a steel sheet electroplated with a zinc-based composite selected from the group consisting of Zn-Ni-SiO₂, Zn-NiZrO₂, Zn-Cr-SiO₂, and Zn-Cr-ZrO₂.
 13. The highly corrosion-resistant, colored thin film-coated steel sheet according to claim 2 wherein said plated steel sheet is a steel sheet electroplated with a zinc alloy selected from the group consisting of Zn-Ni, ZnCr and Zn-Fe.
 14. The highly corrosion-resistant, colored thin film-coated steel sheet according to claim 2 wherein said plated steel sheet is a steel sheet hot-dipped with a zinc alloy selected from the group consisting of Zn-Al, Zn-Mg, and Zn-Ni.
 15. The highly corrosion-resistant, colored thin film-coated steel sheet according to claim 2, wherein said polyamide resin is selected from the group consisting of poly m-phenyleneisophthalamide, and poly-p-phenyleneterephthalamide. 